Кафедра експлуатації та ремонту машин
Permanent URI for this communityhttps://dspace.kntu.kr.ua/handle/123456789/788
Browse
3 results
Search Results
Item Studying the tribological properties of mated materials C61900-A48-25BC1.25BNo.25 in composite oils containing geomodifiers(PC Technology Center, 2019) Aulin, V.; Hrynkiv, A.; Lysenko, S.; Lyashuk, O.; Zamota, T.; Holub, D.; Аулин, В. В.; Гринькив, А. В.; Лысенко, С. В.; Ляшук, О. Л.; Замота, Т. Н.; Голуб, Д. В.; Аулін, В. В.; Гриньків, А. В.; Лисенко, С. В.; Ляшук, О. Л.; Замота, Т. Н.; Голуб, Д. В.Studying the lubricating ability of the basic and composite oils Monnol TS-5 UHPD 10W40+K¬GМF-1+oleic acid, Monnol TS-5 UHPD 10W40+XADO HighWay for Diesel Truck on materials C61900 - A48- 25BC1.25BNo. 25 revealed their positive effect in com¬parison with basic oil Monnol TS-5 UHPD 10W40. This is proved by the enhancement of such characteristics as welding load and critical load, as well as the nature of dependence of the diameter of spots of wear of lower FBM balls on the load applied to them. These composite oils can be used to increase wear resistance of tribojunction of machine parts. It was found that among the studied oils Monnol TS-5 UHPD 10W40+KGМF-1+oleic acid, Monnol TS-5 UHPD 10W40+XADO HighWay for Diesel Truck, com¬posite oil with geomodifier KGМF-1+oleic acid demon¬strated the best result in comparison with the basic oil: wear indicator decreased by 11.5...14.3 %, аnd critical load increased by 17.2 %. The anti-scruff properties, which are determined by welding load, increased by 19.3 %. 3. It was determined that the patterns of changing friction momentum and wear intensity of the samples over time of testing on the friction machine 2070 CMT-1 depend both on their material, type of junction and the lu¬bricating medium. When geomodifier KGМF-1+oleic acid is used in basic oil Monnol TS-5 UHPD 10W40, friction momentum decreases on the mated samples from materi¬als C61900-A48-25BC1.25BNo. 25 by 5...57 %, compared to the basic oil. In addition, it was determined that wear intensity decreases by 3.4...6.0 times for the mated sam¬ples of type I and type III, and by 1.3…1.8 times for the mated samples of type II and type IV. Во время проведения исследований смазочной способности базовой и композиционных масел Monnol TS-5 UHPD 10W40 + КGМF-1 + олеиновая кислота, Monnol TS-5 UHPD 10W40 + XADO HighWay for Diesel Truck на материалах C61900 - A48-25BC1.25BNo.25 выявлены их положительный эффект по сравнению с базовым маслом Monnol TS-5 UHPD 10W40. Об этом свидетельствует повышение таких характеристик, как нагружение сварки и критическое нагружение, а также характер зависимости диаметра пятен износа нижних шариков FBM от приложенной к ним нагрузки. Данные композиционные масла можно использовать для повышения износостойкости трибосопряжений деталей машин. Выявлено, что среди исследуемых композиционных масел Monnol TS-5 UHPD 10W40 + КGМF-1 + олеиновая кислота, Monnol TS-5 UHPD 10W40 + XADO HighWay for Diesel Truck композиционное масло с геомодификаторы КGМF-1 + олеиновая кислота показала лучший результат по сравнению с базовом маслом: показатель износа уменьшился на 11,5 ... 14,3%, а максимальная нагрузка повысилась на 17,2%. Противозадирные свойства, которые определяются нагрузкой сварки, улучшились на 19,3%. Определено, что закономерности изменения момента трения и интенсивности изнашивания образцов со временем испытания на машине трения 2070 СМТ-1 зависят как от их материала, типа сопряжений и смазочного среды. При использовании геомодификаторы КGМF-1 + олеиновой кислоты в базовом масле Monnol TS-5 UHPD 10W40 на сопряжениях образцов из материалов C61900 - A48-25BC1.25BNo.25 на 5 ... 57% снижается момент трения, по сравнению с базовым маслом . При этом определено, что интенсивность изнашивания уменьшается в 3,4 ... 6,0 раза для I и III типа сопряжения образцов, а для ІІ и IV типа сопряжения образцов - в 1,3 ... 1,8 раза. Підчас проведення досліджень мастильної здатності базової та композиційних олив Monnol TS-5 UHPD 10W40+КGМF-1+олеїнова кислота, Monnol TS-5 UHPD 10W40+XADO HighWay for Diesel Truck на матеріалах C61900 – A48-25BC1.25BNo.25 виявлено їх позитивний ефект у порівнянні з базовою оливою Monnol TS-5 UHPD 10W40. Про це свідчить підвищення таких характеристик, як навантажування зварювання та критичного навантажування, а також характер залежності діаметра плям зносу нижніх кульок FBM від прикладеного до них навантаження. Дані композиційні оливи можливо використовувати для підвищення зносостійкості трибоспряжень деталей машин. Виявлено, що серед досліджуваних композиційних олив Monnol TS-5 UHPD 10W40+КGМF-1+олеїнова кислота, Monnol TS-5 UHPD 10W40+XADO HighWay for Diesel Truck композиційна олива з геомодифікатором КGМF-1+олеїнова кислота показала найкращий результат у порівнянні з базовою оливою: показник зносу зменшився на 11,5...14,3 %, а критичне навантаження зросло на 17,2 %. Протизадирні властивості, які визначаються навантаженням зварювання, покращилися на 19,3 %. Визначено, що закономірності зміни моменту тертя та інтенсивності зношування зразків з часом випробування на машині тертя 2070 СМТ-1 залежать як від їх матеріалу, типу спряжень та мастильного середовища. При застосуванні геомодифікатора КGМF-1+олеїнової кислоти в базовій оливі Monnol TS-5 UHPD 10W40 на спряженнях зразків з матеріалів C61900 – A48-25BC1.25BNo.25 на 5...57 % знижується момент тертя, в порівнянні з базовою оливою. При цьому визначено, що інтенсивність зношування зменшується в 3,4...6,0 рази для І і ІІІ типу спряження зразків, а для ІІ і ІV типу спряження зразків - в 1,3...1,8 рази.Item Wear resistance increase of samples tribomating in oil composite with geo modifier КGМF-1(University of Kragujevac, 2019) Aulin, V.; Lysenko, S.; Lyashuk, O.; Hrinkiv, A.; Velykodnyi, D.; Vovk, Y.; Holub, D.; Chernai, A.; Аулін, В. В.; Лисенко, С. В.; Ляшук, О. Л.; Гриньків, А. В.; Великодний, Д. О.; Вовк, Ю. Я.; Голуб, Д. В.; Чернай, А. Є.Increase of wear resistance of different types of tribomating which are functioning in fluid lubrication is possible due to: choosing more expensive and high quality material of samples that is not always sensible; applying some wear resistant coatings on them; selection and formation of complex composition of oil additives. Due to nanomaterials development there is a possibility of efficient use of functional additives such as geo modifiers in tribology. Due to geo modifier-based oil composites use it’s not necessary to make any structural changes of machines mated parts though their wear resistance is increased. It requires the conducting of some experimental tribological research. It was found that oil media modified by a geo modifier increase the wear resistance of working surfaces of different types of tribomating. The use of geo modifier КGМF-1 (Katerynivka friction geo modifier -1 (patent of Ukraine №69657)) has been suggested. Lubrication quality of oil compositions based on М-10Г2К (M-10G2K) (motor oil of 10th viscosity grade, of group Г2К (G2K), for the CIS countries the oil grade conforms SAE 30) + КGМF-1 (4.0 - 4.5%) has been studied on a computer modernized four-ball friction testing machine ЧШМ-К1 (CHMK-К1). To evaluate the lubrication quality of the oil composite with the suggested geo modifier and to use the comparative analysis of the obtained results the research was conducted on commercial samples of base oil M-10G2K and oil composites M-10G2K + XADO Maximum for Diesel Truck (2.0 - 2.3%) (agent 2D sliding revitalization factor (RF) 100, revitalizant 1 Stage RF 100, metal conditioner RF 5.5), M-10G2K + cuprum glycerate (3.7 - 4.5%). Some average indices of wear, critical load, and welding load have been found. Samples division into 4 types of mating according to the following characteristic features: mobility, material hardness and friction area has been suggested for more accurate picture of wear resistance changes of samples tribomating which are functioning in base and modified oil. Lower friction torque of different samples couplings in modified oil by geo modifier КGМF-1 in comparison with base oil M-10G2K was recorded while using Friction machine 2070 SMT-1 with add-on module "ring-ring". The samples wear rate in modified oil by geo modifier КGМF-1 in comparison with base oil M-10G2K was studied by method of acoustic signal amplitude measurements directly from the friction zone by a commercially produced instrument of Brüel & Kjear company. It was found that efficiency increase of the oil compositions under investigation is taking place in the following order: M-10G2K + XADO Maximum for Diesel Truck, M-10G2K + cuprum glycerate, M-10G2K + КGМF-1. Wear index due to the use of modified oil M-10G2K + КGМF-1 was 19 - 20 % lower comparing to the obtained data of the base oil, critical load value was 27 - 29 % larger, and welding load – 24 - 25% larger respectively. Moreover, it was recorded that the maximum wear rate of samples in their functioning in modified oil M-10G2K + КGМF-1 was 3 times lower, and friction torque change law is similar to the wear rate change depending on the time of testing. Підвищення зносостійкості трибоспряжень різних типів спряжень, що функціонують в рідинному мащені, можливе за рахунок: вибору більш якісного і вартісного матеріалу зразків, що не завжди є доцільним; нанесення зносостійких покриттів на них; підбір та формування комплексного складу добавок в оливу. З розвитком наноматеріалів в трибології створилась можливість ефективно використовувати функціональні добавки у вигляді геомодифікаторів. При впровадженні композиційних олив з геомодифікаторами не потрібно виконувати конструктивні зміни спряжень деталей машин, але їх зносостійкість збільшується. Це потребує проведення експериментальних трибологічних досліджень. Виявлено, що модифіковані оливні середовища геомодифікатором підвищують зносостійкість робочих поверхонь різних типів трибоспряжень. Запропоновано використання геомодифікатора КGМF-1 (Катеринівський геомодифікатор тертя – 1 (патент України № 69657)). Досліджували мастильну здатність оливних композицій з основою М-10Г2К (моторна олива 10 класу в'язкості, групи Г2К для країн СНД марка оливи відповідає SAE 30) + КGМF-1 (4,0...4,5%) досліджували на чотири кульковій машині тертя з комп'ютерною модернізацією 1 (ЧШМ-К1). Для оцінки мастильної здатності композиційної оливи з запропонованим геомодифікатором та використанням порівняльного аналізу відповідних результатів дослідження проводили на промислових зразках базової оливи М-10Г2К та композиційних олив М-10Г2К + XADO Maximum for Diesel Truck (2,0...2,3%) (Агент 2D ковзання revitalization factor (RF) 100, ревіталізант 1 Stage RF 100, кондиціонер металу RF 5,5) , М-10Г2К + гліцерату міді (3,7...4,5%). Були виявлені усереднені показники зносу, критичне навантаження та навантаження зварювання. Для більш точного відображення процесу зміни зносостійкості спряжень зразків, що функціонують в базовій та модифікованій оливі, запропоновано поділ зразків в спряженнях на чотири типи за характерними ознаками: рухомість, твердість матеріалу і площа зони тертя. Зменшення моменту сили тертя різних спряжень зразків в модифікованій оливі геомодифікатором КGМF-1 в порівнянні з базовою оливою М-10Г2К фіксували при використанні машини тертя моделі 2070 СМТ-1 з додатковим модулем "кільце-кільце". Дослідження інтенсивності зношування зразків в модифікованій оливі геомодифікатором КGМF-1 в порівнянні з базовою оливою проводили методом вимірювання амплітуди акустичного сигналу безпосередньо із зони тертя за допомогою приладу фірми Brüel & Kjear. Виявлено, що зростання ефективності досліджуваних мастильних композицій спостерігається у наступному порядку: М10-Г2К + XADO Maximum for Diesel Truck, М10-Г2К + гліцерат міді, М10-Г2К + КGМF-1. Показник зносу, при використанні модифікованої оливи М10-Г2К + КGМF-1, у порівнянні з отриманими даними базової оливи зменшився на 19...20 %, значення критичного навантаження збільшилось на 27...29 %, а навантаження зварювання – збільшилось на 24...25%. відповідно. В свою чергу зафіксовано, що максимальна інтенсивність зношування зразків, при їх функціонуванні в модифікованої оливі М10-Г2К + КGМF-1, зменшилась в 3 рази, а закономірність зміни моменту тертя аналогічна зміні інтенсивності зношування від тривалості випробування.Item Вплив присадок до моторних олив на характеристики дизелів, що працюють в нестаціонарних умовах експлуатації(УкрДАЗТ, 2014) Аулін, В. В.; Слонь, В. В.; Голуб, Д. В.; Aulin, V.; Slon, V.; Holub, D.В статті розглянуто вплив присадок на зовнішньо-швидкісні характеристики дизелів, що працюють в нестаціонарних умовах. Виявлено збільшення рівня потужності та крутного моменту і зниження питомої витрати палива при додаванні присадок дисульфід молібдена, "НИОД-5", "Roil Gold, і "КГМТ-1" запропонованої авторами. Отримані результати обґрунтовуються впливом присадок на характеристики та властивості моторної оливи, її зношувальну здатність та припрацьованість основних спряжень дизелі. Визначено також відновлюваний характер властивостей оливи при додаванні присадок, що підтверджують експериментальні дослідження зміни моменту тертя з напрацюванням в різних режимах функціонування: безперервному і "пуск-зупинка". The article considers the influence of additives on the externally-speed characteristics of diesel engines operating under transient conditions. Investigations were carried out on the break-in-roller stand КС-276-032 to validate the running-in and testing of diesel engines in the cold no-load and hot load and no load. Testing procedures and evaluate the performance of the engine. In the basic engine oil added various functional additives in optimum concentrations. Speed range crankshaft commensurate with the operational range. Tests were carried out in a continuous mode, and the "start-stop". Revealed that the addition of molybdenum disulphide additives, "НИОД-5", "Roil Gold", and "КГМТ-1" suggested by the authors, increased levels of power and torque and reduced fuel consumption. The findings substantiate the influence of additives on the characteristics and properties of the engine oil, it wears capacity and runningmates main diesel. Restorative properties of the oil with the addition of additives, is supported by experimental studies of changes in the friction torque with operating in different modes of operation: continuous and "start-stop". In the used motor oil without making the test additives friction torque peaks recorded in a continuous mode and in the "start-stop". When making additive remained initial peak friction torque in continuous operation at the beginning of each period mode "start-stop". To some extent reduce the overall level of the friction torque value. The characteristic is that the moment of friction in the reduction of oil additives of magnitude lower than in the continuous mode.