Browsing by Author "Kropivna, A."
Now showing 1 - 13 of 13
Results Per Page
Sort Options
Item Specific Distribution of Thermal Effects of Graphite Forming Reactions in High-strength Cast Iron(ЦНТУ, 2020) Kropivnyi, V.; Bosyi, M.; Kuzyk, O.; Kropivna, A.; Кропівний, В. М.; Босий, М. В.; Кузик, О. В.; Кропівна, А. В.; Кропивный, В. Н.; Босый, Н. В.; Кузык, А. В.; Кропивная, А. В.The dependence of thermal effects of reactions in the formation of inclusions of vermicular and globular graphite is substantiated in the article. The calculation of thermal effects according to the heat of formation of reagents in cast iron and their dependence on the temperature factor is given. The distribution of temperatures and carbon content in the eutectic shell is shown, increasing the compact inclusion of graphite due to diffusing carbon from the melt through the austenitic shell. Питання механізму формування кулястого графіту все ще залишаються дискусійним та не дає досягнути загальноприйнятного теоретичного пояснення протікаючих явищ. Розкриття механізму процесів формування кулястого графіту сприятиме відкриттю широких можливостей управління структурою і властивостями високоміцного чавуну. Таким чином, метою даної роботи є уточнення ролі теплових ефектів реакцій в процесі кристалізації аустеніту і формуванні включень графітну у модифікованому високоміцному чавуні. Дослідження мікроструктури показало, що розміщенні включення кулястого графіту навіть безпосередньо біля внутрішньої поверхні кірки знаходяться в оточенні феритної оболонки. Включення вермикулярного графіту виходять на поверхню розділу торцями, які оточені феритом лише по бокам. Це свідчить, що торці включень компактного та вермикулярного графіту в окремі періоди процесу кристалізації мали контакт з розплавом. Таким чином, після формування зародка кулястого графіту відбувається повне оточення його аустенітною оболонкою, а при формуванні вермикулярного графіту лише часткове. Згідно з методикою розрахунку теплових ефектів реакцій за теплотою утворення реагентів в чавуні, кількість теплоти, яка виділяється при кристалізації аустенітної фази по межі поділу "розплав – аустеніт" становить 76,69 кДж на 1кг розплаву. Відповідно, кількість тепла, яке виділяється на межі "аустеніт - компактне графітне включення" складає 15,39 кДж на 1 кг розплаву. Тобто, оточуюча включення компактного графіту тверда аустенітна фаза буде мати суттєво вищу температуру ніж оточуючий її розплав. Особливі теплофізичні умови формування аустенітних оболонок приводить до підвищеного вмісту у них кремнію та пониженого марганцю, наслідком чого є формування феритних оболонок навколо включень компактного графіту. Обґрунтовано залежність теплових ефектів реакцій у формуванні включень вермикулярного та кулястого графіту. Наведено розрахунок теплових ефектів за теплотою утворення реагентів в чавуні та встановлено їх залежність від температурного фактору. Показано розподіл температур та вмісту вуглецю в евтектичній оболонці, ростучого компактного включення графіту за рахунок дифузії вуглецю з розплаву через аустенітну оболонку. В статье приведен расчет тепловых эффектов с теплотой образования реагентов в чугуне и установлено их зависимость от температурного фактора. Обоснована роль теплофизических процессов в формировании включений вермикулярного и шаровидного графита, с обеспечением их роста за счет диффузии углерода из расплава через аустенитную оболочку.Item The influence of titanium as a desferoidizing element on the stability of production of magnesium cast irons with compacted graphite(University of Kragujevac, 2021) Aulin, V.; Kropivny, V.; Kuzyk, O.; Lyashuk, O.; Bosyi, M.; Vovk, Y.; Kropivna, A.; Sokol, M.; Senyk, A.; Slobodyan, L.; Аулін, В. В.; Кропівний, В. М.; Кузик, О. В.; Ляшук, О. Л.; Босий, М. В.; Вовк, Ю. Я.; Кропівна, О. В.; Сокол, М. Б.; Сеник, А. А.; Слободян, Л. М.The thermodynamic calculations and the obtained dependence of the Gibbs energy of the reactions of formation of titanium oxide, titanium sulfide, titanium nitride and titanium carbide in the melt of magnesium cast iron on their concentrations and melt temperature have been presented in the article. It has been shown that titanium, regardless of the concentration in melt, will primarily perform a deoxidizing effect, interacting with the oxygen. The lower negative values of the Gibbs energies are characterized by the reactions of the interaction of titanium with sulfur, at a concentration of the latter 0.01%, which indicates a decrease in the probability of such reaction occurrence. From a thermodynamic point of view, the reactions of titanium nitride and carbide formation are less probable. The values of the Gibbs energy of the interaction reaction of titanium depend to a large extent on the melt temperature. It has been found that for a more complete realization of the desulfurizing properties of titanium, it is advisable to enter the composition of cast iron during melting and overheating, when the melt temperature reaches maximum values. The optimal conditions for obtaining magnesium cast irons with compacted graphite has been determined. It has been found that the addition of titanium to magnesium cast iron, as a desferoidizing element containing 0.035% S, has a positive effect on stabilizing the formation of compacted graphite. В статті представлені термодинамічні розрахунки і одержана залежність енергії Гіббса реакцій утворення оксида титана, сульфіда титана, нітрида титана і карбіда титана в розплаві магнієвого чавуну від їх концентрацій і температури розплаву. Показано, що титан, незалежно від концентрації у розплаві, в першу чергу, буде виконувати розкислюючу дію, взаємодіючи з киснем. Меншими від’ємними значеннями енергій Гіббса характеризуються реакції взаємодії титана з сіркою, при концентрації останньої 0.01%, що свідчить про зниження ймовірності протікання такої реакції. З термодинамічної точки зору в меншій мірі ймовірне протікання реакцій утворення нітридів і карбідів титана. Значення енергії Гіббса реакції взаємодії розчинених у залізі титана і сірки в найбільшій мірі залежать від температури розплаву. Виявлено, що для більш повної реалізації десульфуруючих властивостей титан доцільно вводити до складу чавуну в період плавки та перегріву, коли температура розплаву досягає максимальних значень. Визначено оптимальні умови одержання магнієвих чавунів з вермикулярним графітом. З’ясовано, що добавка титана у магнієвий чавун, як десфероідизуючого елемента, що містить 0.035% S, позитивно впливає на стабілізацію формування компактного (вермикулярного) графіту.Item Аналіз та гармонізація національних до міжнародних стандартів якісних показників чавунів з вермикулярним графітом(ЦНТУ, 2020) Кропівна, А. В.; Кузик, О. В.; Kropivna, A.; Kuzyk, O.; Кропивная, А. В.; Кузык, А. В.В статті розглянуто національні та міжнародні стандарти якісних показників чавуну з вермикулярним графітом. Дано аналіз діючим стандартам в Україні ДСТУ на чавун з вермикулярним графітом а також регламентовані його механічні властивості та рекомендований хімічний склад. Проаналізовано властивості аналогічних міжнародних та європейських стандартів на чавун з вермикулярним графітом згідно стандартизації ISO, SAE, CEN, VDG, ASTM, JIS, GB, STAS, а також наведено перехресні посилання на стандарт ISO 16112 до інших стандартних марок ЧВГ. З’ясована відповідність марок матеріалів, в залежності від їх хімічного складу та механічних властивостей, наведених в ГОСТах, міжнародних та європейських показників. Ensuring and coordination of high quality indicators of materials in the foundry industry is necessary in the development of Ukraine's economy. High quality products need to be enshrined in new national standards, harmonized with international and European standards. Thus, the purpose of this work is to analyze national and international standards for quality indicators of vermicular graphite iron and their harmonization with each other. The foundry industry of Ukraine has developed mainly with the use of interstate standards - GOST, which differ significantly from European and international and requires coordination and other approaches to the development of new standards. Today there are a number of international standards: ISO, SAE, CEN, VDG, ASTM, JIS, GB, STAS, which regulate the properties of cast iron with vermicular graphite. Most standards define the range of permissible content of spherical graphite (0… 20%) in the structure of cast iron with vermicular graphite, as well as determine the shape of samples to determine the properties and provide for the determination of graphite on surfaces formed after machining castings. In accordance with the needs of the automotive industry, the Society of Automotive Engineers (SAE) has created the standard SAEJ1887 JUL2002 for cast iron with vermicular graphite. The DSTU standard in force in Ukraine regulates only the temporary resistance to tensile and elongation laid down in the brand designation. Thus, the improvement, provision and harmonization of the national standard at the vermicular graphite iron by achieving high quality indicators of materials in the foundry industry, will ensure the stability of the technological production process, and further entry into international and European markets and a qualitatively new level of domestic engineering. An analysis of the current standards in Ukraine DSTU for cast iron with vermicular graphite is given, as well as its regulated mechanical properties and recommended chemical composition. The properties of similar international and European standards for cast iron with vermicular graphite according to ISO, SAE, CEN, VDG, ASTM, JIS, GB, STAS standardization are analyzed, as well as cross-references to ISO 16112 to other standard brands of the vermicular graphite iron. The conformity of brands of materials, depending on their chemical composition and mechanical properties given in GOST, international and European indicators is found out. В статье рассмотрены национальные и международные стандарты качественных показателей чугуна с вермикулярным графитом. Дан анализ действующим стандартам в Украине ДСТУ на чугун с вермикулярным графитом а также регламентированы его механические свойства и рекомендован химический состав. Проанализированы свойства аналогичных международных и европейских стандартов на чугун с вермикулярным графитом согласно стандартизации ISO, SAE, CEN, VDG, ASTM, JIS, GB, STAS, а также приведены перекрестные ссылки на стандарт ISO 16112 к другим стандартных марок ЧВГ. Выяснено соответствие марок материалов, в зависимости от их химического состава и механических свойств, приведенных в ГОСТах, международных и европейских показателей.Item Пристрій для фрикційно-механічного нанесення покриттів(ДП “Український інститут промислової власності”, 2012) Чернявський, О. В.; Шепеленко, І. В.; Василенко, І. Ф.; Красота, М. В.; Кропівна, А. В.; Cherniavskyi, O.; Shepelenko, I.; Vasylenko, I.; Krasota, M.; Kropivna, A.Корисна модель належить до нанесення антифрикційних покриттів і може бути використана як в машинобудуванні, так і в ремонтному виробництві.Item Роль теплофізичних процесів формування структури високоміцних чавунів(2017) Аулін, В. В.; Кропівний, В. М.; Кузик, О. В.; Кропівна, А. В.; Босий, М. В.; Aulin, V.; Kropivnyi, V.; Kuzyk, O.; Kropivna, A.; Bosyi, M.В статті наведено розрахунок теплових ефектів за теплотою утворення реагентів в чавуні та встановлено їх залежність від температурного фактору. Обґрунтовано роль теплофізичних процесів у формуванні включень вермикулярного та кулястого графіту, із забезпеченням їх росту за рахунок дифузії вуглецю з розплаву через аустенітну оболонку. In the article the calculation of thermal effects with the heat of formation of reagents in cast iron is given and their dependence on the temperature factor is established. The role of thermo physical processes in the formation of inclusions of vermicular and globular graphite is substantiated, ensuring their growth due to the diffusion of carbon from the melt through the austenite shell.Item Система технологій. Практичні роботи(ЦНТУ, 2024) Кузик, О. В.; Кропівний, В. М.; Кропівна, А. В.; Молокост, Л. А.; Kuzyk, O.; Kropivnyi, V.; Kropivna, A.; Molokost, L.Основною метою дисципліни покладено вироблення у студентів навичок системного підходу до оцінки технології виготовлення будь-якого виробу на основі відомих початкових даних (кількість та якість продукту, наявність сировини, устаткування, стан технології та сучасних технологічних доробок, вартість устаткування та сировини, екологічна безпека, попит ринку, тощо). The main goal of the discipline is to develop students' skills in a systematic approach to assessing the manufacturing technology of any product based on known initial data (quantity and quality of the product, availability of raw materials, equipment, state of the art and modern technological developments, cost of equipment and raw materials, environmental safety, market demand, etc.).Item Спосіб комбінованої обробки поверхонь тертя(ДП “Український інститут промислової власності”, 2012) Черновол, М. І.; Шепеленко, І. В.; Чернявський, О. В.; Посвятенко, Е. К.; Кропівна, А. В.; Chernovol, M.; Shepelenko, I.; Cherniavskyi, O.; Posviatenko, E.; Kropivna, A.Корисна модель належить до комбінованої обробки внутрішніх циліндричних поверхонь тертя і може бути використана в машинобудуванні, а також у ремонтному виробництв і при відновленні зношених деталей.Item Спосіб комбінованої обробки поверхонь тертя(2012-11-12) Черновол, М. І.; Шепеленко, І. В.; Чернявський, О. В.; Посвятенко, Е. К.; Кропівна, А. В.; Chernovol, M.; Shepelenko, I.; Cherniavskyi, O.; Posviatenko, E.; Kropivna, A.Спосіб комбінованої обробки поверхонь тертя передбачає попередню механічну обробку, нанесення регулярного мікрорельєфу та його заповнення антифрикційним матеріалом, причому всі операції виконуються за один прохід інструмента. Способ комбинированной обработки поверхностей трения предусматривает механическую обработку, нанесение регулярного микрорельефа и его заполнение антифрикционным материалом, причем все операции выполняются за один проход инструмента. A method for combination processing of friction faces comprises the mechanical operation, application of regular microrelief and it filling with antifriction material, at that all operations are performed in single pass of tool.Item Спосіб модифікування чавуну(ЦНТУ, 2018-05-25) Кропівний, В. М.; Аулін, В. В.; Кузик, О. В.; Кропівна, А. В.; Карпушин, С. О.; Молокост, Л. А.; Kropivnyi, V.; Aulin, V.; Kuzyk, O.; Karpushyn, S.; Kropivna, A.; Malokost, L.Спосіб модифікування чавуну, що включає завантаження гранульованого магнію у реакційну камеру ливникової системи ливарної форми з наступним заливанням чавуну через реакційну камеру і розчиненням модифікатора, який відрізняється тим, що магнієву лігатуру попередньо піддають плакуванню нанографітом.Item Спосіб нанесення антифрикційних покриттів на внутрішні циліндричні поверхні(ДП “Український інститут промислової власності”, 2012) Черновол, М. І.; Шепеленко, І. В.; Чернявський, О. В.; Василенко, І. Ф.; Кропівна, А. В.; Chernovol, M.; Shepelenko, I.; Cherniavskyi, O.; Vasylenko, I.; Kropivna, A.Корисна модель належить до нанесення антифрикційних покриттів на внутрішні циліндричні поверхні тертя деталей.Item Спосіб нанесення антифрикційних покриттів на внутрішні циліндричні поверхні(2012-11-12) Черновол, М. І.; Шепеленко, І. В.; Чернявський, О. В.; Василенко, І. Ф.; Кропівна, А. В.; Chernovol, M.; Shepelenko, I.; Cherniavskyi, O.; Vasylenko, I.; Kropivna, A.Спосіб нанесення антифрикційних покриттів на внутрішні циліндричні поверхні, при якому при його виконанні застосовується принцип протягування, який здійснюється шляхом зворотно-поступального руху інструмента з одночасним дискретним обертанням деталі. Способ нанесения антифрикционных покрытий на внутренние цилиндрические поверхности, при котором при его выполнении применяется принцип протягивания, который осуществляется путем возвратно-поступательного движения инструмента с одновременным дискретным вращением детали. A method for application of antifriction coatings on internal cylindrical surfaces, at which drawing principle, is used by reciprocal movement of tool with simultaneous discrete turning of a detail.Item Спосіб підвищення питомого робочого об'єму шестеренних гідромашин(2009-03-25) Кулєшков, Ю. В.; Руденко, Т. В.; Осін, Р. А.; Кропівна, А. В.; Кулєшкова, К. Ю.; Kulieshkov, Y.; Rudenko, T.; Osin, R.; Kropivna, A.; Kulieshkova, K.Спосіб підвищення питомого робочого об'єму шестеренних гідромашин належить до машинобудування і може бути використаний при виробництві шестеренних гідромашин. Способ повышения удельного рабочего объема шестеренных гидромашин относится к машиностроению и может быть использован при производстве шестеренных гидромашин. A method for increase of specific working volume of pinion hydro-machines relates to machine-building and can be used at production of pinion hydro-machines.Item Формування структури високоміцних чавунів при виготовленні деталей мобільної сільськогосподарської і автотранспортної техніки(ЦНТУ, 2017-11) Аулін, В. В.; Кропівний, В. М.; Кузик, О. В.; Кропівна, А. В.; Босий, М. В.; Aulin, V.; Kropivnyi, V.; Kuzyk, O.; Kropivna, A.; Bosyi, M.